Case hardened round steel chains

Round steel chain

Type G80E10 / G80E14/ G40 E10 / G40 E14


Highly wear resistant, deep case hardened round steel chains and components are produced due to the use of special steels
(CrNi, CrNiMo, MnC) and optimised heat treatments. Even if the chains have a high surface hardness of 800 HV10 the chains
have high core strength- and breaking strength values to achieve a greater fatigue strength.
Chains and all components are matched regarding to their wear characteristics, to minimize the wear and to provide the greatest
possible wear life and maximum chain life.
 


 

Delicious Bookmark this on Delicious


Güteklasse G80 E10 G80 E14
Bruchspannung (N/mm2) 400 350
Prüfspannung (N/mm2) 240 210
Bruchdehnung ca. (%) 2 2
Oberflächenhärte HV 10 800 800
Aufkohlungstiefe HTÄ ... d +/- 0,01d 0,1 0,14
Einsatzhärtungstiefe EHT 550 HV 3 ... d min. 0,06 0,09
Werkstoff bis d = 22 mm : CrNi-legiert
ab d = 26 mm : CrNiMo-legiert
Güteklasse G40 E10 G40 E14
Bruchspannung (N/mm2) 250 210
Prüfspannung (N/mm2) 125 105
Bruchdehnung ca. (%) 2 2
Oberflächenhärte HV 10 800 800
Aufkohlungstiefe HTÄ ... d +/- 0,01d 0,1 0,14
Einsatzhärtungstiefe EHT 550 HV 3 ... d min. 0,063 0,09
Werkstoff MnCr-legiert
Güteklasse G40 E10 G80 E10
Bruchspannung (N/mm2) 250 350
Prüfspannung (N/mm2) 125 210
Bruchdehnung ca. (%) 2 2
Oberflächenhärte HV 10 750 750
Aufkohlungstiefe HTÄ ... d +/- 0,01d 0,1 0,1
Einsatzhärtungstiefe EHT 550 HV 3 ... d min. 0,06 0,06
Werkstoff Mn-legiert CrNi-legiert